ER836 – EH275
Filled, hot curing, low shrinkage, epoxy casting resin system for encapsulation of medium voltage electrical switchgear equipment by gravity vacuum casting and pressure gelation.
Description
Colour: Resin: Brown
Hardener: Clear Amber Anhydride
Viscosity: Hardener 200 mPa.s
Mixing Ratio: ER836 100,0 by weight
EH275 20,0
Pot Life: 6 to 8 hours at 40 Deg. C. and 30 minutes at 80 Deg C.
Gelation Time: 14 minutes at 120 Deg. C (Test tube Gelnorm DIN 16945)
Post Curing: 12 hours at 130 Deg. C
Warm resin ER836 to 50 to 60 deg. C and add hardener at room temperature. Mix well under vacuum. Pour into pressure pot and keep it at 40 deg C for pressure gelation. For conventional casting, warm resin to 80 to 90 deg. C, add hardener and mix well under vacuum.
CHARACTERISTICS after CURE
(Approximate values)
Impact: 9 – 11 KJ/m2
Flexural Strength: 110 – 130 MPa
Elongation: 6 – 8%
Tensile Strength: 70 – 80 MPa
Elongation %: 1 – 2 %
Dielectric Strength: 15 (20 s) KV/mm
Heat Distortion Temperature: 110 – 120 Deg. C
Comparative Tracking: 400 V
Volume Resistivity: 8×10>15 Ohm cm
Tan Delta: 0,01972
Permitivity: 4,14
The above data are offered for customer’s guidance only. It implies no guarantee. Customers must conduct their own tests to determine the suitability of the material for their specific applications.
Date: V20.1 1 Feb 2020