LP73 – LH96Z Epoxy Laminating Paste

LP73 – LH96Z Laminating Paste

 

LP73 / LH96Z is an epoxy laminating paste reinforced with chopped strand fibre-glass designed for reinforcement of epoxy tools and moulds. Packed in two parts, the paste LP73 has a low density and is very easy to apply. May be applied up to thickness of 10 to 40 mm.

Viscosity may be reduced by mixing with laminating system ER20 and EH96 (mixing ratio 100: 20)

 

Description

 

Colour:                Resin LP 73:             Grey

                               Hardener LH96Z:     Blue

 

Mixing Ratio:      

LP73           100,0     20,0  kg   by weight

LH96Z        8,0         1,6  kg    

 

Pot Life:                                  45 to 60 minutes at 25 Deg. C

 

Curing Time:                          5 to 8 hours at 25 Deg. C (500 Grams)

 

Demoulding Time:                  24 hours

 

CHARACTERISTICS after CURE

 

Hardness:                                         75 Shore D after 7 days at 25 Deg. C

 

Heat Distortion Temperature:         50 Deg. C

Density:                                            1,10

Impact Strength:                              7 KJ/m2

Compressive Strength:                     50 MPa

Flexural Strength:                            30 to 40 MPa

Linear Shrinkage:                            0,2 to 0,4 %            

Date Issued: 1 January 2009

The above data are offered for customer’s guidance only. It implies no guarantee. Customers must conduct their own tests to determine the suitability of the material for their spec